May 20, 2011 Friday 15:30
Hüseyin Kurt, Trinity College, Dublin
New perpendicular thin films for spintronics & high density magnetic recording

Abstract: There is a renewed interest in magnetic materials that exhibit uniaxial, out-of-plane anisotropy due to their high spin injection efficiency and their high thermal stability. The next generation of scalable magnetic memory and logic will integrate such materials as the active elements. Heusler alloys, such as Co2MnSi, are widely studied due to their nearly half metallic spin polarization, making it possible to reduce the critical current in spin torque switched MRAMs. Tetragonal (t) Heusler alloys offer the possibility to provide high thermal stability in addition to high spin polarization. t-Mn2MnGa (Mn3Ga) is a tetragonal Heusler alloy with a calculated spin polarization of 88% at the Fermi level. It crystallizes in the D022 structure composed of alternating planes of Mn in X(Y) positions in a bct Ga cage. It is a nearly compensated ferrimagnet with an easy c-axis, and the Curie temperature is higher than 770 K, where the material undergoes a first order structural transition to the hexagonal D019 phase. After an introduction discussing different perpendicular magnetic anisotropy systems and the physics of spintronic devices, I will present our recent results on epitaxial films of stoichiometric t- Mn3Ga, with a measured spin polarization of 58% (point contact Andreev reflection). These films exhibit high coercivity (1.8 T), low magnetization (110 kA/m) and high anisotropy constant (Ku=0.89 MJ/m3), which can support thermally stable perpendicular bits down to 10 nm in size. Their low magnetization allows for easy switching by spin torque while their high coercive field makes them immune to the fields generated by even the strongest permanent magnets. No magnetic shielding is required. t-Mn2Ga films also crystallize in D022 structure with Mn deficiency in the unit cell. This composition has a high magnetization (470kA/m) combined with a high anisotropy constant (Ku=2.35 MJ/m3); properties potentially useful for high-density magnetic recording with areal densities up to 10 Tb per square inch in bit patterned media. The magnetization and anisotropy in the D022 alloys depend on both the stoichiometry and the site occupancy of Mn atoms. Substitutional doping in the Mn2MnGa Heusler structure could allow us to engineer magnetic materials for a specific application.

CV:
1994-99, BSc Physics, Bogazici University
2000-05, PhD Physics 2005, Michigan State University
PhD Thesis on Current perpendicular to plane giant magnetoresistance and spin torque switching in magnetic nanopillars
2005-07, Postdoc, Rowland Institute, Harvard University
Carbon nanotube and silicon nanowire based logic devices
2008-now Postdoc, Trinity College Dublin
· Spin filtering in MgO based tunnel junctions
· Superlattice based perpendicular anisotropy in magnetic thin films
· Tetragonal Heusler alloys for spintronic devices and high density magnetic recording